Abstract

Quartz powder is used in ultra-high-performance concrete to improve granular packing, but repeated inhalation during manufacture can cause health issues. The mechanical properties of UHPC are influenced by the post-setting curing method. A hypothesis suggests limestone powder could be a viable filler to mitigate these issues under three different curing regimes, replacing quartz powder of similar size. The study assessed 18 mixtures with different w/b ratios for flow characteristics and compressive strength after 7 and 28 days of curing under various conditions. Limestone powder positively impacted compressive strength and had fresh properties. A two-factor interaction model accurately correlated variables and responses. Numerical optimization was performed to find the optimal mixture with proper flow and the highest compressive strength. The use of 150 kg/m3 of locally sourced limestone powder in the mixture with a w/b ratio equal to 0.198 and a 48hr-90°C curing regime can be considered the optimal amount to secure the greatest modeling compressive strength (169.10 MPa at 7 days and 181.71 MPa at 28 days), fulfilling the limit values of spread flow (220 mm) with the increasing percentage ratio of 67% and 49% at 7-days and 28-days ages under 90°C heat curing when the w/b equals 0.198.

References

H. Akeed et al., Ultra-high-performance fiber-reinforced concrete. Part I: Developments, principles, raw materials, Case Stud. Constr. Mater., 17 (2022) e01290. https://doi.org/10.1016/j.cscm.2022.e01290 M. Azmee and N. Shafiq, Ultra-high performance concrete: From fundamental to applications, Case Stud. Constr. Mater., 9 (2018) e00197. https://doi.org/10.1016/j.cscm.2018.e00197 Wu, J. Li, and Y. Su, Development of ultra-high performance concrete against blasts: from materials to structures. Woodhead Publishing, 2018. Ç. Yalçınkaya and O. Çopuroğlu, Hydration heat, strength and microstructure characteristics of UHPC containing blast furnace slag, J. Build. Eng., 34 (2021) 101915. https://doi.org/10.1016/j.jobe.2020.101915 Arora, A. Almujaddidi, F. Kianmofrad, B. Mobasher, and N. Neithalath, Material design of economical ultra-high performance concrete (UHPC) and evaluation of their properties, Cem. Concr. Compos., 104 (2019) 103346. https://doi.org/10.1016/j.cemconcomp.2019.103346 D. Salahaddin, J. H. Haido, and G. Wardeh, The behavior of UHPC containing recycled glass waste in place of cementitious materials: A comprehensive review, Case Stud. Constr. Mater., 17 (2022) e01494. https://doi.org/10.1016/j.cscm.2022.e01494 D. Redondo-Mosquera, D. Sánchez-Angarita, M. Redondo-Pérez, J. C. Gómez-Espitia, and J. Abellan-Garcia, Development of high-volume recycled glass ultra-high-performance concrete with high C3A cement, Case Stud. Constr. Mater., 18 (2023) e01906. https://doi.org/10.1016/j.cscm.2023.e01906 A. Soliman and A. Tagnit-Hamou, Using glass sand as an alternative for quartz sand in UHPC, Constr. Build. Mater., 145 (2017) 243-252. https://doi.org/10.1016/j.conbuildmat.2017.03.187 F. Burroughs, J. Shannon, T. S. Rushing, K. Yi, Q. B. Gutierrez, and D. W. Harrelson, Potential of finely ground limestone powder to benefit ultra-high performance concrete mixtures, Constr. Build. Mater., 141 (2017) 335-342. https://doi.org/10.1016/j.conbuildmat.2017.02.073 Abellán, J. Fernández, N. Torres, and A. Núñez, Statistical optimization of ultra-high-performance glass concrete, ACI Mater. J., 117 (2020) 243-254. https://doi.org/10.14359/51720292 -H. Kang, Y. Jeong, K. H. Tan, and J. Moon, The use of limestone to replace physical filler of quartz powder in UHPFRC, Cem. Concr. Compos., 94 (2018) 238-247. https://doi.org/10.1016/j.cemconcomp.2018.09.013 Soliman and A. Tagnit-Hamou, Development of ultra-high-performance concrete using glass powder–Towards ecofriendly concrete, Constr. Build. Mater., 125 (2016) 600-612. https://doi.org/10.1016/j.conbuildmat.2016.08.073 A. Mosaberpanah and O. Eren, Effect of quartz powder, quartz sand and water curing regimes on mechanical properties of UHPC using response surface modelling, Adv. Concr. Constr., 5 (2017) 481-492. https://doi.org/10.12989/acc.2017.5.5.481 Huang, H. Kazemi-Kamyab, W. Sun, and K. Scrivener, Effect of cement substitution by limestone on the hydration and microstructural development of ultra-high performance concrete (UHPC), Cem. Concr. Compos., 77 (2017) 86-101. https://doi.org/10.1016/j.cemconcomp.2016.12.009 Hernández-Carrillo, A. Durán-Herrera, and A. Tagnit-Hamou, Optimization of Ultra-High-Performance Concrete Using Soft and Hard Inert Fillers (Limestone and Quartz), ACI Mater. J., 119 (2022) 275-288. https://doi.org/10.14359/51734222 P. Li, H. Brouwers, W. Chen, and Q. Yu, Optimization and characterization of high-volume limestone powder in sustainable ultra-high performance concrete, Constr. Build. Mater., 242 (2020) 118112. https://doi.org/10.1016/j.conbuildmat.2020.118112 K. Aswed, M. S. Hassan, and H. Al-Quraishi, Effects of Curing Temperature and Chemical Admixture Type on Fresh Properties and Compressive Strength of Ultra High-performance Concrete, Eng. Technol. J., 40 (2022) 1448-1454. http://doi.org/10.30684/etj.2022.132300.1103 R. Prem, A. Ramachandra Murthy, and B. H. Bharatkumar, Influence of curing regime and steel fibres on the mechanical properties of UHPC, Mag. Concr. Res., 67 (2015) 988-1002. https://doi.org/10.1680/macr.14.00333 -H. Kang, S.-G. Hong, and J. Moon, Shrinkage characteristics of heat-treated ultra-high performance concrete and its mitigation using superabsorbent polymer based internal curing method, Cem. Concr. Compos., 89 (2018) 130-138. https://doi.org/10.1016/j.cemconcomp.2018.03.003 Reda, N. Shrive, and J. Gillott, Microstructural investigation of innovative UHPC, Cem. Concr. Res., 29 (1999) 323-329. https://doi.org/10.1016/S0008-8846(98)00225-7 Wang, C. Shi, Z. Wu, J. Xiao, Z. Huang, and Z. Fang, A review on ultra high performance concrete: Part II. Hydration, microstructure and properties, Constr. Build. Mater., 96 (2015) 368-377. https://doi.org/10.1016/j.conbuildmat.2015.08.095 P. C. Association, Ultra High Performance Concrete (UHPC) Guide to Manufacturing Architectural Precast UHPC Elements, National Precast Concrete Association: Carmel, CA, USA, 2013. I. Khuri and S. Mukhopadhyay, Response surface methodology, Wiley Interdiscip. Rev. Comput. Stat., 2 (2010) 128-149. https://doi.org/10.1002/wics.73 Ghafari, H. Costa, and E. Júlio, RSM-based model to predict the performance of self-compacting UHPC reinforced with hybrid steel micro-fibers, Constr. Build. Mater., 66 (2014) 375-383. https://doi.org/10.1016/j.conbuildmat.2014.05.064 ASTM, Standard specification for Portland cement (ASTM-C150/C150M), West Conshohocken, Pennsylvania: ASTM International., A. S. f. T. a. M. International, (2015a). ASTM, Standard specification for silica fume used in cementitious mixtures (ASTM C1240-15), West Conshohocken, Pennsylvania: ASTM International., A. S. f. T. a. M. International, (2015b). ASTM, Standard test method for flow of hydraulic cement mortar (ASTM C1437), West Conshohocken, Pennsylvania: ASTM International., A. S. f. T. a. M. International, (2020a). ASTM, Standard test method for compressive strength of hydraulic cement mortars using 2-in. or 50-mm cube specimens (ASTM C109/C109M-11b). West Conshohocken, Pennsylvania: ASTM International., A. S. f. T. a. M. International, (2010a). M. Rashad, An exploratory study on alkali-activated slag blended with quartz powder under the effect of thermal cyclic loads and thermal shock cycles, Constr. Build. Mater., 70 (2014) 165-174. https://doi.org/10.1016/j.conbuildmat.2014.06.097 M. Rashad and A. S. Ouda, An investigation on alkali-activated fly ash pastes modified with quartz powder subjected to elevated temperatures, Constr. Build. Mater., 122 (2016) 417-425.https://doi.org/10.1016/j.conbuildmat.2016.06.068 A.-G. N. T.-C. D. C. Jaramillo-Murcia and E. García-Castaño, Properties Analysis of Ultra-High-Performance Concrete with Recycled Glass and Limestone Powders, ACI Matet. J., 119 (2022) 153-164. https://doi.org/10.14359/51736006 Wu, C. Shi, and W. He, Comparative study on flexural properties of ultra-high performance concrete with supplementary cementitious materials under different curing regimes, Constr. Build. Mater., 136 (2017) 307-313. https://doi.org/10.1016/j.conbuildmat.2017.01.052 Yu, P. Spiesz, and H. Brouwers, Mix design and properties assessment of ultra-high performance fibre reinforced concrete (UHPFRC), Cem. Concr. Res., 56 (2014) 29-39. https://doi.org/10.1016/j.cemconres.2013.11.002

Highlights

Quartz powder can be removed from ultra-high-performance concrete (UHPC) mixtures The inclusion of limestone powder in UHPC mixtures substantially improves compressive strength A 48hr-90°C curing regime is optimal for achieving the highest compressive strength

DOI

10.30684/etj.2023.143595.1598

First Page

493

Last Page

504

Download

Share

COinS